LNP? THERMOCOMP? LC008EXQ compound
聚醚醚酮
40% 碳纖維增強(qiáng)材料
SABIC Innovative Plastics
產(chǎn)品說(shuō)明:
LNP THERMOCOMP LC008EXQ is a compound based on Polyetheretherketone containing 40% Carbon Fiber. Added features of this grade include: Electrically Conductive, Easy Molding.
Also known as: LNP* THERMOCOMP* Compound LC008EXQ
Product reorder name: LC008EXQ
|
填料/增強(qiáng)材料 |
· 碳纖維增強(qiáng)材料, 40% 填料按重量 |
|||
|
特性 |
|
|||
|
加工方法 |
· 注射成型 |
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
比重 |
1.44 |
|
ASTM D792 |
|
收縮率 |
|
|
ASTM D955 |
|
流動(dòng) : 24小時(shí) |
1.5E-3 到 3.0E-3 |
in/in |
|
|
橫向流動(dòng) : 24小時(shí) |
7.0E-3 到 0.014 |
in/in |
|
|
吸水率 (24 hr, 50% RH) |
0.050 |
% |
ASTM D570 |
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 |
|
|
|
|
-- 2 |
6.02E+6 |
psi |
ASTM D638 |
|
-- |
5.86E+6 |
psi |
ISO 527-2/1 |
|
抗張強(qiáng)度 |
|
|
|
|
斷裂 3 |
47900 |
psi |
ASTM D638 |
|
斷裂 |
46600 |
psi |
ISO 527-2/5 |
|
伸長(zhǎng)率 |
|
|
|
|
斷裂 3 |
1.5 |
% |
ASTM D638 |
|
斷裂 |
1.4 |
% |
ISO 527-2/5 |
|
彎曲模量 |
|
|
|
|
1.97 in 跨距 4 |
5.11E+6 |
psi |
ASTM D790 |
|
-- 5 |
4.91E+6 |
psi |
ISO 178 |
|
彎曲應(yīng)力 |
|
|
|
|
-- |
66700 |
psi |
ISO 178 |
|
斷裂, 1.97 in 跨距 4 |
71400 |
psi |
ASTM D790 |
|
壓縮強(qiáng)度 |
31200 |
psi |
內(nèi)部方法 |
|
剪切模量 |
726000 |
psi |
ASTM C273 |
|
剪切強(qiáng)度 |
18300 |
psi |
ASTM C273 |
|
泊松比 |
|
|
|