LNP? THERMOCOMP? LC006EXQ compound
聚醚醚酮
30% 碳纖維增強材料
SABIC Innovative Plastics
產(chǎn)品說明:
LNP THERMOCOMP LC006EXQ is a compound based on Polyetheretherketone containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.
Also known as: LNP* THERMOCOMP* Compound LC006EXQ
Product reorder name: LC006EXQ
|
填料/增強材料 |
· 碳纖維增強材料, 30% 填料按重量 |
|||
|
特性 |
|
|||
|
加工方法 |
· 注射成型 |
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|
比重 |
1.40 |
|
ASTM D792 |
|
收縮率 |
|
|
ASTM D955 |
|
流動 : 24小時 |
1.5E-3 到 3.0E-3 |
in/in |
|
|
橫向流動 : 24小時 |
7.0E-3 到 0.014 |
in/in |
|
|
吸水率 (24 hr, 50% RH) |
0.050 |
% |
ASTM D570 |
|
機械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
|
|
|
|
-- 2 |
4.60E+6 |
psi |
ASTM D638 |
|
-- |
5.12E+6 |
psi |
ISO 527-2/1 |
|
抗張強度 |
|
|
|
|
斷裂 3 |
45500 |
psi |
ASTM D638 |
|
斷裂 |
46300 |
psi |
ISO 527-2/5 |
|
伸長率 |
|
|
|
|
斷裂 3 |
1.7 |
% |
ASTM D638 |
|
斷裂 |
1.5 |
% |
ISO 527-2/5 |
|
彎曲模量 |
|
|
|
|
1.97 in 跨距 4 |
3.93E+6 |
psi |
ASTM D790 |
|
-- 5 |
3.95E+6 |
psi |
ISO 178 |
|
彎曲應(yīng)力 |
|
|
|
|
-- |
66300 |
psi |
ISO 178 |
|
斷裂, 1.97 in 跨距 4 |
69200 |
psi |
ASTM D790 |
|
剪切模量 |
690000 |
psi |
ASTM C273 |
|
剪切強度 |
17300 |
psi |
ASTM C273 |
|
泊松比 |
|
|
|