| 詳細(xì)參數(shù) | |||
|---|---|---|---|
| 品牌/廠(chǎng)家 | Orevac法國(guó)阿科瑪 | 類(lèi)型 | 正牌料 |
| 用途級(jí)別 | 薄膜級(jí) | 加工級(jí)別 | 吹塑級(jí) |
| 特性級(jí)別 | 耐高溫 | 外觀顏色 | 黑色 |
| 密度 | 0.943g/cm3 | 拉伸強(qiáng)度 | 48kg |
| 彎曲強(qiáng)度 | 59kg | 缺口沖擊強(qiáng)度 | 25kg.cm |
| 斷裂伸長(zhǎng)率 | 700到900% | 成型收縮率 | 87% |
| 熔體流動(dòng)速率 | 6.0到8.0,g/10min | ||
Orevac® T 9318
乙烯醋酸乙烯共聚物
Arkema
產(chǎn)品說(shuō)明:
OREVAC® T 9318 is a random terpolymer of ethylene, vinyl acetate and maleic anhydride made by high-pressure radicalar polymerization process. As an ethylene copolymer, OREVAC® T 9318 is compatible with PE in all proportions, and with most other ethylene copolymers. Vinyl acetate brings softness, flexibility and polarity, maleic anhydride gives reactivity, leading to versatile adhesive properties to polar and non polar substrates. As a result of high-pressure polymerisation in tubular reactor, OREVAC® T 9318 exhibits high transparency (low haze).
Applications
OREVAC® T 9318 can be used to produce thermo-adhesive films for solid substrates like PA, PET & PU films, aluminium foils, fiber mats, foams... OREVAC® T 9318 is also suitable as a tie layer between polyethylene and polyamide in blown film, cast film or in tubes coextrusion. It can be used as a coupling agent in cables compounds bulations.
|
供貨地區(qū) |
|
|||
|
特性 |
|
|||
|
用途 |
|
|||
|
加工方法 |
|
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
密度 |
0.943 |
g/cm3 |
ISO 1183, ASTM D1505 |
|
熔流率（熔體流動(dòng)速率） (190°C/2.16 kg) |
6.0 到 8.0 |
g/10 min |
ASTM D1238, ISO 1133 |
|
醋酸乙烯含量 |
17.0 到 20.0 |
wt% |
|
|
Maleic Anhydride Content |
1600 |
ppm |
內(nèi)部方法 |
|
硬度 |
額定值 |
單位制 |
測(cè)試方法 |
|
肖氏硬度 (邵氏 A, 15 秒, 0.110 in, 模壓成型) |
88 |
|
ASTM D2240, ISO 868 |
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
抗張強(qiáng)度 |
|
|
|
|
斷裂, 0.110 in, 模壓成型 2 |
3190 |
psi |
ASTM D638 |
|
斷裂, 0.110 in, 模壓成型 |
3190 |
psi |
ISO 527-2/5A/50 |
|
伸長(zhǎng)率 |
|
|
|
|
斷裂, 0.110 in, 模壓成型 2 |
700 到 900 |
% |
ASTM D638 |
|
斷裂, 0.110 in, 模壓成型 |
|
|
|